Abstract
This paper analyses the influence of processing temperatures of polyamide 6.6 Grivory type HTV-3H1 noir 9205, polyamide 6.6 Grivory type HTV-45H1 noir 9205 and polyamide 6.6 Grivory type HTV-6H1 noir 9205 on some mechanical properties, when injecting items used in various technical articles. The test-specimens on PA 6.6 Grivory type HTV-3H1 noir 9205 were molded at the following injection temperatures: 310, 320, 330, 340 and 350°C. The test-specimens on PA 6.6 Grivory type HTV-45H1 noir 9205 were molded at the following injection temperatures: 320, 330, 340, 350 and 360°C. The test-specimens on PA 6.6 Grivory type HTV-6H1 noir 9205 were molded at the following injection temperatures: 330, 340, 350, 360 and 370°C. These specimens were tested using methods for determination of the following mechanical properties: tensile strength, Izod impact strength and hardness (Shore). For all these polymers, it was determined that increasing of injection temperature results in insignificant changes of hardness. The Izod impact strength decreases with increasing the injection temperature. After reaching the minimum value, Izod impact strength increases again if the processing temperature is raised further. The tensile strength at break increases with increasing the processing temperature. After reaching the maximum value, tensile strength at break decreases if the processing temperature is raised further. Keywords: polyamide 6.6 (PA 6.6), tensile tests, Izod impact test, Shore Durometer hardness test