Abstract
The aim of this work was to find the influence of the addition of low amount of hydrophilic and hydrophobic TiO2 nanoparticles on compressive strength, microhardness and rheological properties of flowable dental composite material. Specimens were prepared by adding 0.05; 0.2 and 1 wt. % of hydrophilic and hydrophobic 20 nm TiO2 nanoparticles. These specimens were compared to non-modified control specimens in compressive strength and microhardness. Furthermore, their rheological properties were determined. The optimal nanoparticle loading was 0.2 % hydrophobic TiO2, resulting in significantly higher compressive strength and microhardness than those of the control specimen group. Mechanical properties of flowable composites reinforced with hydrophilic and hydrophobic TiO2 at higher loadings are lower than those of control specimens, which is the result of nanoparticle agglomeration. TiO2 nanoparticles addition resulted in the decrease in viscosity in all specimens except for the specimewn with 1% hydrophilic TiO2 nanoparticles. In accordance to the obtained results, hydrophobic nanoparticle addition results in a more resistant and durable material, combined with an increased flowability compared to a non-modified composite.
Keywords: flow composite; TiO2 nanoparticles; mechanical properties; rheological properties