Abstract
To analyze the implant overdentures components as following: morphology and composition aspects of several small diameter systems, evaluating both the implant and the retention system (1); biomechanical characteristics of some of the polymers used for manufacturing the overdenture base (2). An experimental in vitro study was carried out through optic microscopy to analyze the metallic structure of dental implants components and anchor systems. The marketed products analyzed were mini1SKY (Bredent) and 3M ESPE MDI Mini dental implant (3M ESPE). A Zeiss microscope with Kohler illumination was used. Samples from polymeric materials commonly used for overdenture based (i.e. Duracryl and Superacryl) were analyzed by 3 point bending test by Tira device. In the case of the mini1SKY system (Bredent), the dental implant has the typical structure of marketed pure titanium that went through thermomechanical processing, resulting in a higher rate of granulation, and the matrix has a completely different structure, as it is a monophasic structure specific to materials that crystalize in the cubic system of the stainless steels. In the case of the 3M ESPE MDI system, the implant and the matrix have a similar microstructure, specific to a Ti-6Al-4V beta alloy annealed with an extremely fine rate of granulation. Duracryl and Superacryl samples fractured variable (frequently close to the midline) and were similar in regard to the value of breaking force. Knowledge of the materials of the components of implant overdenture guide their selection from the point of view of biocompatibility, resistance and ensuring denture retention.
Keywords: dental implants; attachment system; in vitro; edentulism