Abstract
Hand layup was used to fabricate the glass fibre reinforced aluminium foam epoxy composites in this study. On the manufactured materials, dry sliding wear experiments were performed. The effect of wearprocess parameters such asapplying load (kg), speed (m/s), and sliding distance (m) on specific wear rate (Ws) was investigatedand the obtained results were compared with neat glass fibre reinforced epoxy composite in this work. The outcome of these results showed that specific wear rate (Ws) of glassfibre epoxy composite containing aluminium foam decreased as compared with neat glass fibre reinforced polymer composites. Experimental results showed that a minimum wear rate of 10.1 µm was attained for the sliding velocity (1.5 m/s), Applied load (2 kg), and sliding distance (1000 m) in the fabricated composite laminates. It was observed thatthe resistance to wear in glass fibre reinforced aluminium foam composite was mainly due to the bond strength between aluminium foam and epoxy.
Keywords: polymer composite; epoxy resin; wear rate; glass fibre; aluminium foam