ABOUT INDEXING EDITORIAL BOARD ARCHIVES AUTHOR GUIDELINES SUBMIT PAPER NEWS, EVENTS AUTHOR'S PAGE CONTACT
Materiale Plastice
Cite as: Mater. Plast.
https://doi.org/10.37358/Mat.Plast.1964

OSIM Nr. R102356
ISSN Print 0025-5289
ISSN Online 2668-8220
Materiale Plastice - Latest Issue

Latest Issue >>>
ARCHIVES
   Volume 61, 2024
   Volume 60, 2023
   Volume 59, 2022
   Volume 58, 2021
   Volume 57, 2020
   Volume 56, 2019
   Volume 55, 2018
   Volume 54, 2017
   Volume 53, 2016
   Volume 52, 2015
   Volume 51, 2014
   Volume 50, 2013
   Volume 49, 2012
   Volume 48, 2011
   Volume 47, 2010
   Volume 46, 2009
   Volume 45, 2008
   Volume 44, 2007
   Volume 43, 2006
   Volume 42, 2005
   Volume 41, 2004
   Volume 40, 2003
 
<<<< back

Materiale Plastice (Mater. Plast.), Year 2015, Volume 52, Issue 1,





Gheorghe Radu Emil MAries Processing Temperatures Influence of Three Types of Polyamide 6.6 Reinforced with Different Percentages of Fiber Glass on Some Mechanical Properties


Abstract:
This paper analyses the influence of processing temperatures of polyamide 6.6 Grivory type HTV-3H1 noir 9205, polyamide 6.6 Grivory type HTV-45H1 noir 9205 and polyamide 6.6 Grivory type HTV-6H1 noir 9205 on some mechanical properties, when injecting items used in various technical articles. The test-specimens on PA 6.6 Grivory type HTV-3H1 noir 9205 were molded at the following injection temperatures: 310, 320, 330, 340 and 350°C. The test-specimens on PA 6.6 Grivory type HTV-45H1 noir 9205 were molded at the following injection temperatures: 320, 330, 340, 350 and 360°C. The test-specimens on PA 6.6 Grivory type HTV-6H1 noir 9205 were molded at the following injection temperatures: 330, 340, 350, 360 and 370°C. These specimens were tested using methods for determination of the following mechanical properties: tensile strength, Izod impact strength and hardness (Shore). For all these polymers, it was determined that increasing of injection temperature results in insignificant changes of hardness. The Izod impact strength decreases with increasing the injection temperature. After reaching the minimum value, Izod impact strength increases again if the processing temperature is raised further. The tensile strength at break increases with increasing the processing temperature. After reaching the maximum value, tensile strength at break decreases if the processing temperature is raised further. Keywords: polyamide 6.6 (PA 6.6), tensile tests, Izod impact test, Shore Durometer hardness test



Issue: 2015 Volume 52, Issue 1
Pages:
Publication date: 2015/3/30
download pdf   Download Pdf Article
Creative Commons License
This article is published under the Creative Commons Attribution 4.0 International License


Downloads number: 0
<<<< back
 
  Search Authors
Crossref Member Badge
 DOI  logo
 Gold Open Access | Source=http://www.plos.org/  | Author=art designer at PLoS
Creative Commons License