ABOUT INDEXING EDITORIAL BOARD ARCHIVES AUTHOR GUIDELINES SUBMIT PAPER NEWS, EVENTS AUTHOR'S PAGE CONTACT
Materiale Plastice
Cite as: Mater. Plast.
https://doi.org/10.37358/Mat.Plast.1964

OSIM Nr. R102356
ISSN Print 0025-5289
ISSN Online 2668-8220
Journal Metrics
* Impact factor 2019: 1.517
* 5-Year IF: 1.179
* CiteScore: 2.4
* H index: 22
Materiale Plastice - Latest Issue

Latest Issue >>>
ARCHIVES
   Volume 58, 2021
   Volume 57, 2020
   Volume 56, 2019
   Volume 55, 2018
   Volume 54, 2017
   Volume 53, 2016
   Volume 52, 2015
   Volume 51, 2014
   Volume 50, 2013
   Volume 49, 2012
   Volume 48, 2011
   Volume 47, 2010
   Volume 46, 2009
   Volume 45, 2008
   Volume 44, 2007
   Volume 43, 2006
   Volume 42, 2005
   Volume 41, 2004
   Volume 40, 2003
 
<<<< back

Materiale Plastice (Mater. Plast.), Year 2006, Volume 43, Issue 2,





Poly-1,3,4,-oxadiazole -ethers Thin Films.


Abstract:
Thin films, in the range of tens of micrometers thickness, have been prepared by casting onto glass plates the chloroform or N-methylpyrrolidone solutions of poly(1,3,4-oxadiazole-ether)s. The polymers have been prepared by nucleophyilic substitution polymerization technique of 2,5-bis(p-fluorophenyl)-1,3,4-oxadiazole with various aromatic bisphenols, such as 4,4’-isopropylidenediphenol, 4,4’-(1,4-phenylene-diisopropylidene)bisphenol or 4,4’-(hexafluoroiso-propylidene)diphenol. They showed high thermal stability with decomposition temperature above 410°C and glass transition temperature in the range of 187-211°C. The polymer films exhibited good mechanical properties with tensile strengths in the range of 36.92- 44.50 MPa, tensile modulus in the range of 1.42-1.74 GPa and elongation at break in the range of 3-91%. Electrical insulating properties of polymer films were evaluated on the basis of dielectric constant. The values of the dielectric constant at 10 kHz were in the range of 2.98-3.18. Keywords: poly(1,3,4-oxadiazole-ether)s, thin films, mechanical properties, dielectric constant



Issue: 2006 Volume 43, Issue 2
Pages:
Creative Commons License
This article is published under the Creative Commons Attribution 4.0 International License
<<<< back
 
  Search Authors
Crossref Member Badge
 DOI  logo
 Gold Open Access | Source=http://www.plos.org/  | Author=art designer at PLoS
Creative Commons License