ABOUT INDEXING EDITORIAL BOARD ARCHIVES AUTHOR GUIDELINES SUBMIT PAPER NEWS, EVENTS AUTHOR'S PAGE CONTACT
Materiale Plastice
Cite as: Mater. Plast.
https://doi.org/10.37358/Mat.Plast.1964

OSIM Nr. R102356
ISSN Print 0025-5289
ISSN Online 2668-8220
Materiale Plastice - Latest Issue

Latest Issue >>>
ARCHIVES
   Volume 61, 2024
   Volume 60, 2023
   Volume 59, 2022
   Volume 58, 2021
   Volume 57, 2020
   Volume 56, 2019
   Volume 55, 2018
   Volume 54, 2017
   Volume 53, 2016
   Volume 52, 2015
   Volume 51, 2014
   Volume 50, 2013
   Volume 49, 2012
   Volume 48, 2011
   Volume 47, 2010
   Volume 46, 2009
   Volume 45, 2008
   Volume 44, 2007
   Volume 43, 2006
   Volume 42, 2005
   Volume 41, 2004
   Volume 40, 2003
 
<<<< back

Materiale Plastice (Mater. Plast.), Year 2011, Volume 48, Issue 1,





Camelia Cerbu, IOAN CURTU Mechanical Characterization of the Glass Fibres / Rubber / Resin Composite Material


Abstract:
The paper proposes a way of using of the recycled rubber for the manufacturing of a hybrid composite material based on epoxy resin, reinforced both with glass woven fabrics and with recycled rubber. One presents the mechanical characteristics of this composite material, measured in: flexural test by using the method of the three points and impact testing with Charpy pendulum. The work also describes some aspects concerning to the effects of the water absorption on the mechanical behaviour in flexural testing after 2980 h (124 days) of immersion in water, at room temperature. Finally, the experimental results obtained were comparatively analysed for both the dried and wet specimens. One could remark a degradation of the mechanical characteristics (elastic modulus E, flexural strength s, mechanical work W until the maximum force). Concerning the impact behaviour, it was measured the failure energy U and then computed the resilience K (impact strength). It was observed that additionally reinforcing with rubber particles leads to the increasing of the resilience K. Keywords: hybrid composite; recycled rubber; absorption; bending; impact



Issue: 2011 Volume 48, Issue 1
Pages:
download pdf   Download Pdf Article
Creative Commons License
This article is published under the Creative Commons Attribution 4.0 International License


Downloads number: 0
<<<< back
 
  Search Authors
Crossref Member Badge
 DOI  logo
 Gold Open Access | Source=http://www.plos.org/  | Author=art designer at PLoS
Creative Commons License